Car Paint, Resin for Car Paint, Refinish Paint manufacturer / supplier in China, offering Hot Selling China Factory Price Liquid Coating Color Matte Blue Car Paint, Hot Sale and Durable Car Paint Polyurethane Paint for Cars, Epoxy Primer Price 2K Car Paint and so on.
Min. Order / Reference FOB Price | |
---|---|
100 KG | US $3.50/ KG |
Local Area: | Shaoguan, Guangdong, China |
---|---|
R&D Capacity: | OEM, ODM, Other |
Payment Terms: | LC, T/T, PayPal, WesternUnion |
Color: | - |
---|---|
Appearance: | Liquid |
Main Raw Material: | Nitrocellulose, Polyurethane |
Features:
High solid content, strongcovering, good sanding, colored viscous liquid, suitable for all coloredOptical Fiber, Cable & Wire furniture, decoration primer coating.
The film can make the surface flat, smooth, with good adhesion, dry etc.
Technical Parameters
SolidContent
60-80%
Mix Ratio
1:0.5: 0.6-0.8
100 part PU Primer
50 part PU Hardener
60-80 part Thinner
Viscosity( after mix with thinner)
13-18seconds (4 cups)
Skin Dry Time
5~10minutes (25ºC, humidity 75%)
Sanding Time
4-6hours (25ºC, humidity 75%)
PU Solid Color Primer &PU High Glossy Solid Color Top Coat
Features:
This series of products with high solid content, high fullness, heat resistance, acid and alkali resistance, solvent resistance, light resistance, strong adhesion, a water white transparent viscous liquid, suitable for indoor decoration and furniture surface coating operation, can also be added to the solvent dye, as coating color repair paint.
Technical Parameters
SolidContent
65-70%
Mix Ratio
1:0.8: 0.8-1100 part PU Primer80 part PU Hardener80-100 part Thinner
Viscosity( after mix with thinner)
12-15seconds (4 cups)
Skin Dry Time
20~25minutes (25ºC, humidity 75%)
Fully Dry Time
24hours (25ºC, humidity 75%)
PU Matt Clear Top Coat &PU Matt Solid Color Top Coat
Features:
This series of products with good transparency, gloss and natural, delicate touch, smooth, good fullness, strong adhesion for high-grade furniture series of transparent matte finish the final coating finish, can also add solvent dyes, as repair color engineering and independent use of color Drilling Rig transparent topcoat coating.
Technical ParCleaning Machine ameters
SolidContent
60-65%
Mix Ratio
1:0.5: 0.8-1100 part PU Primer80 part PU Hardener80-100 part Thinner
Viscosity( after mix with thinner)
12-15sLean Pipe & Pipe Rack System econds (4 cups)
Skin Dry Time
15minutes (25ºC, humidity 75%)
FSealing & Gaskets ully Dry Time
24hours (25ºC, humidity 75%)